Uncured Properties
Resin [Part A] |
|
|
| Viscosity |
|
6700 cps |
| Specific Gravity |
|
1.32 |
| Color |
|
 Black |
Uncured Properties
Hardener [Part B] |
|
|
| Viscosity |
|
4700 cps |
| Specific Gravity |
|
0.986 |
| Color |
|
 Clear,
amber tint |
| Cured Properties - PHYSICAL |
Test Method |
Result |
| Volume Mix Ratio (resin:hardener) |
|
1.94 : 1 |
| Mass Mix Ratio (resin:hardener) |
|
2.40 : 1 |
| Working time (100g) |
|
120 min. |
| Cure Time (100g, room temp.) |
|
24 hours |
| Heat Cure Time (100g, 65°C) |
|
60 min. |
| Shore Hardness |
|
80 shore D |
Tensile Strength |
ASTM-D-638-02A |
6000 psi |
| Elongation |
ASTM-D-638-02A |
5% |
| Compressive Strength |
ASTM-D-695-02A |
9565 psi |
| Flexural Strength |
ASTM-D-790-03 |
9532 psi |
| Cantilever beam (IZOD) impact |
ASTM-D-256-02 |
0.60 ft lb / in |
| Shear Strength |
ASTM-D-732-02 |
3559 psi |
| Burn Rate |
|
14.2 mm / min |
| |
UL HB |
Pass |
| Cured Properties - TEMPERATURE |
|
|
| Constant Service Temperature |
|
80°C (176°F) |
| Intermediate Service Temperature |
|
90°C (194°F) |
| Heat deflection temperature |
ASTM-D-648-01 |
62.2°C (144°F) |
| Cured Properties - ELECTRICAL |
|
|
| Breakdown voltage |
ASTM-D-149-97A |
31,100 volts |
Dielectric Strength |
ASTM-D-149-97A |
838 volts/mil |
| Surface resistivity |
ASTM-D-257-99 |
3.8 x 1016 ohm · cm |
| Volume resistivity |
ASTM-D-257-99 |
8.14 x 1016 ohm · cm |
| Dielectric constant |
ASTM-D-150-98 |
3.01 |
| Dissipation factor |
ASTM-D-150-98 |
0.0121 |
| Insulative |
|
Yes |
| Conductive |
|
No |
| Chemical and Solvent Resistance |
Change after
3 days |
Change after
45 days |
| |
|
|
| Hydrocloric Acid |
< 1% |
< 2% |
| Isopropyl Alcohol |
< 1% |
< 1% |
| Ethyl Lactate |
< 5% |
< 15% |
| Acetone |
< 15% |
Destroyed |
| Xylene |
< 15% |
< 20% |
| Iso hexanes |
~ 0% |
< 1% |
| Mineral spirits |
~ 0% |
~ 0% |