| Standards |
| UL Registered |
Flame Class 94V-0, category QMFZ2 |
file # E334302 |
| Uncured
Properties - Resin [Part A] |
| Viscosity |
@ 24°C Brookfield 30 RPM Spindle 4 |
4000 cps |
| Phase |
|
Liquid |
| Color |
|
Black |
| Specific
Gravity |
|
1.34 kg/l |
| Odor |
|
Mild |
| Flash Point |
|
190 °C |
| Uncured
Properties - Hardener [Part B] |
| Viscosity |
@ 24°C Brookfield 30 RPM Spindle 4 |
14000 cps |
| Phase |
|
Liquid |
| Color |
|
Grey |
| Specific
Gravity |
|
1.17 kg/l |
| Odor |
|
Musty |
| Flash Point |
|
105 °C |
| Uncured Properties – Mixed |
| Viscosity |
@ 20°C Brookfield 50 RPM Spindle 4 |
11500 cps |
| Specific
Gravity |
|
1.28 kg/l |
| Color |
|
Black |
| Mixing Ratio (Part A & B) |
| Volume Mixing Ratio |
|
2 (resin) : 1 (hardener) |
| Mass Mixing Ratio |
|
2 (resin) : 1 (hardener) |
| Working Time |
|
1 hour |
| Curing Time (100 g) |
|
|
 @ room temperature |
|
24 hours |
| @ 65°C / 149 °F |
|
60 minutes |
| @ 80°C / 176 °F |
|
45 minutes |
| @ 100°C / 212 °F |
|
35 minutes |
| Cured
Properties - Physical |
Tensile Impact
@ 0.117 “ thickness |
ASTM D1822
UL 746A |
20.54 kJ/m2 |
| Izod Impact |
ASTM D256 Method A
or ISO 180 |
1.10 kJ/m2 |
| Flexual Strength |
ASTM D790
or ISO 178 |
40.2 Mpa |
| Compressive Strength |
ASTM D695 |
1310 kg/cm2 |
| Lap shear Strength |
ASTM 790
or ISO 178 |
59.3 kg/cm2 |
| Hardness (shore D) |
|
83-84 |
| Flame Class |
UL 746A |
94 V-0 |
| Cured
Properties - Electrical |
Surface Resistivity
@ 23°C/35%RH |
ASTM D257 |
2 x 1015 Ohms/square |
Volume Resistivity
@ 23°C/50%RH |
ASTM D257
UL 746A |
2.71 x 1015 Ohms- cm |
Dielectric Strength
(tested @1.730mm) |
ASTM D149
UL 746A |
19.37 kV/mm |
| Dielectric Constant / Dissipation Factor (tested @ 161") |
ASTM D150-98 |
|
| @ 60 Hz |
|
3.45 / 0.018 |
| @ 1 KHz |
|
3.40 / 0.012 |
| @ 10 KHz |
|
3.31 / 0.013 |
| @ 100 KHz |
|
3.25 / 0.014 |
| @ 1 MHz |
|
3.18 / 0.014 |
| Hot Wire Ignition (HWI) |
ASTM D3874 / TEC 60659-2-20/ UL746A |
52.83 Seconds |
| High- Current Arc Ignition (HAI) |
UL 746A |
94.80 Arcs |
| High Voltage Arc tracking Rate (HVTR) |
UL 746A |
48.07 mm/min |
| High Voltage, low current, Dry Arc Resistance |
ASTM D495
UL 746A |
37.62 seconds |
| Comparative Tracking Index (CTI) |
ASTM D495
UL 746A |
600 -250 V |
| High voltage Arc resistance to Ignition (HVAR) |
UL 746A |
4.67 Seconds |
| Cured
Properties - Thermal |
| Tg (Glass Transition Temp.) |
ASTM D3418 |
56 °C |
| HDT (Heat Deflection Temp.) |
ASTM D648, ISO 75 |
51.9 °C |
| Maximum withstand Temperature |
|
-65 °C to 225 °C |
| Constant Service Temperature |
|
175 °C |
| Operating Temperature Range |
|
-40 °C to 175 °C |
| Cured
Properties - Additional Properties |
| Outgassing |
ASTM E595 |
|
| Total mass loss (TML) |
|
1.45 % |
| Collected Volatile condensable Material (CVCM) |
|
0.03 % |
| Water Vapour Regain (WVR) |
|
0.10 % |
| Ash content |
ISO 3451/1 |
1.27 % |
| |
UL746A |
|
TDS